Tanks the other hard part

The Rocket Equation has a term that is the rocket motor efficiency and a term that is the mass ratio. In a pressure fed system the biggest component of that mass ratio is the tank.
If I could make a tank identical to a 2L soda bottle only 5 to 10 times bigger that would be almost ideal. I could probably find a mechanism, to join a bunch 2L soda bottles and I may pursue that, but I'm also going to try my hand at composite tanks. Toward that end I made mold forms for a 6" diameter cylindrical test tank mold. I heated it up and waxed it with mold release and setup the vacuum bag etc.. got ready for my first composite test part.

I have something non-rocket to do tonight, but tomorrow I hope to try making my first composite part since the solar plane project.

The first tanks will have glued Mylar liners that are not H2O2 safe, but the flight tanks will have mylar/PET liners with no glue. The jury is still out if the tanks will be seamed via vacuum heat, sonic welding, or RF welding.In addition to the liner I also want the tank to be chemically resistant to the H2O2. I want any liner failures to not be immediately catastrophic.

I'm getting a bunch of samples and setting up to do compatibility testing next weekend out at FAR. I'm testing glass, kevlar and carbon fibers with normal epoxy, vinyl ester and special chemically resistant vinyl ester resins. My gut says that plain E glass with the chem compatible resin will be fine, I'm almost certain that carbon with epoxy won't be. I hope the Kevlar and chem resistant resin also work as the kevlar is a bunch stronger than the glass.

Its a multi part test, start with 30% and work your way up to heated 85 or 90%. Anything past 50% really has to be done remotely. I'm planning to soak samples in PET soda bottle bottoms. sitting in hot water on a hot plate. The sample will have a string and pulley so I can pull the sample out of the solution remotely and shoot it with the 243. I could set up some kind of hammer and anvil test, but I worry that if it goes bang, the hammer becomes a projectile.

I figure I'll get the preliminary screening done this weekend and the samples that pass will get the hotplate test in two weeks.